关键波长处的光学常数

632.8 nm (He-Ne)

n = 2.6848

k = 0.0000

589.3 nm (Na-D)

n = 2.6966

k = 0.0000

532 nm

n = 2.7198

k = 0.0000

1550 nm (通讯)

n = 2.6085

k = 0.0000

n, k 色散曲线

数据表（采样）

波长 (μm)	n	k
0.4047	2.82886	0.00000
0.4431	2.78509	0.00000
0.4815	2.75341	0.00000
0.5199	2.72961	0.00000
0.5583	2.71120	0.00000
0.5967	2.69662	0.00000
0.6351	2.68483	0.00000
0.6735	2.67514	0.00000
0.7119	2.66705	0.00000
0.7504	2.66022	0.00000
0.7888	2.65437	0.00000
0.8272	2.64932	0.00000
0.8656	2.64492	0.00000
0.9040	2.64104	0.00000
0.9424	2.63759	0.00000
0.9808	2.63451	0.00000
1.0192	2.63174	0.00000
1.0576	2.62922	0.00000
1.0960	2.62692	0.00000
1.1344	2.62481	0.00000
1.1728	2.62285	0.00000
1.2112	2.62104	0.00000
1.2496	2.61934	0.00000
1.2880	2.61774	0.00000
1.3264	2.61624	0.00000
1.3649	2.61481	0.00000
1.4033	2.61344	0.00000
1.4417	2.61214	0.00000
1.4801	2.61089	0.00000
1.5185	2.60968	0.00000
1.5569	2.60851	0.00000
1.5953	2.60738	0.00000
1.6337	2.60627	0.00000
1.6721	2.60519	0.00000
1.7105	2.60413	0.00000
1.7489	2.60309	0.00000
1.7873	2.60207	0.00000
1.8257	2.60106	0.00000
1.8641	2.60006	0.00000
1.9025	2.59907	0.00000
1.9409	2.59808	0.00000
1.9793	2.59711	0.00000
2.0178	2.59614	0.00000
2.0562	2.59517	0.00000
2.0946	2.59420	0.00000
2.1330	2.59323	0.00000
2.1714	2.59227	0.00000
2.1906	2.59178	0.00000

上表为采样数据（共 94 个数据点），点击"下载完整 CSV"获取全部数据。

数据说明

4H-SiC (hexagonal crystal structure); Extraordinary ray (e)

参考文献

S. Wang, M. Zhan, G. Wang, H. Xuan, W. Zhang, C. Liu, C. Xu, Y. Liu, Z. Wei, X. Chen. 4H-SiC: A new nonlinear material for midinfrared lasers. Laser Photonics Rev. 7, 831–838 (2013)

SiC (e) 折射率

关键波长处的光学常数

n, k 色散曲线

数据表（采样）

数据说明

参考文献

相关材料（主要）

需要测量 SiC (e) 薄膜厚度？

SiC (e) 折射率

关键波长处的光学常数

n, k 色散曲线

数据表（采样）

数据说明

参考文献

相关材料（主要）

需要测量 SiC (e) 薄膜厚度？

验证后下载

下载次数已达上限